Clinical trials are normally performed with well-known brands of glass ionomer cement (GIC), but the cost of these materials is high for public healthcare in less-affluent communities. Given the need to research cheaper materials, it seems pertinent to investigate the retention rate of a low-cost GIC applied as atraumatic restorative treatment (ART) sealants in two centers in Brazil. Four hundred and thirty-seven 6-to-8-year-old schoolchildren were selected in two cities in Brazil. The children were randomly divided into two groups, according to the tested GIC applied in the first permanent molars. The retention rate was evaluated after 3, 6 and 12 months. Kaplan-Meier survival analysis and the log-rank test were performed. The variables were tested for association with sealant longevity, using logistic regression analyses (α = 5%). The retention rate of sealants after 12 months was 19.1%. The high-cost GIC brand presented a 2-fold-more-likely-to-survive rate than the low-cost brand (p < 0.001). Significant difference was also found between the cities where the treatments were performed, in that Barueri presented a higher sealant survival rate than Recife (p < 0.001). The retention rate of a low-cost GIC sealant brand was markedly lower than that of a well-known GIC sealant brand.

The purpose of the present study was to evaluate the erosive potential of different types (concentrated and powdered) and commercial brands of industrialised grape juices. The pH of all five fruit drinks was measured at two time points: immediately after preparation and 24 hours later. Sixty specimens of bovine enamel were randomly allocated and immersed in different types of grape juice (n = 10) for 10 minutes four times a day for fifteen days. The enamel alteration was analysed using surface Knoop microhardness (KHN) and surface roughness (Ra) tests at baseline and on the 5th, 10th and 15th days of the experiment. Two way ANOVA, Tukey's post hoc and Pearson's correlation tests were used for statistical analysis (α = 5%). The grape juices presented pH values ranging from 2.9 to 3.5. All of the tested juices promoted significant enamel mineral loss (p < 0.05) on the first evaluation (5th day of immersion) and produced a significant increase in the mean roughness from the 10th day on when compared to the control group (p < 0.05). By the 15th day, all of the beverages had produced surface roughnesses that were significantly higher than that of the control group. The results suggest that all grape juices, regardless of their commercial presentation, present erosive potential.

This in vitro study evaluated the bond strength of adhesive restorative materials to sound and eroded dentin. Thirty-six bovine incisors were embedded in acrylic resin and ground to obtain flat buccal dentin surfaces. Specimens were randomly allocated in 2 groups: sound dentin (immersion in artificial saliva) and eroded dentin (pH cycling model - 3× / cola drink for 7 days). Specimens were then reassigned according to restorative material: glass ionomer cement (KetacTM Molar Easy Mix), resin-modified glass ionomer cement (VitremerTM) or adhesive system with resin composite (Adper Single Bond 2 + Filtek Z250). Polyethylene tubes with an internal diameter of 0.76 mm were placed over the dentin and filled with the material. The microshear bond test was performed after 24 h of water storage at 37ºC. The failure mode was evaluated using a stereomicroscope (400×). Bond strength data were analyzed with two-way ANOVA and Tukey's post hoc tests (α = 0.05). Eroded dentin showed bond strength values similar to those for sound dentin for all materials. The adhesive system showed the highest bond strength values, regardless of the substrate (p < 0.0001). For all groups, the adhesive/mixed failure prevailed. In conclusion, adhesive materials may be used in eroded dentin without jeopardizing the bonding quality. It is preferable to use an etch-and-rinse adhesive system because it shows the highest bond strength values compared with the glass ionomer cements tested.